For the carbon steel slag, originating from an EAF, three particle sizes were studied (05 mm, 2040 mm, 40185 mm). The ferrochrome slag was crushed and sieved to a 49 mm fraction. The stainless steel slag is a finegrained fraction ( 500 µm) obtained after a crushing, screening and demetallisation treatment. For the characterization